17-4 PH® Stainless Steel, UNS S17400

ASTM A564, ASTM 693, AMS 5523, AMS 5604, AMS 5643 17-4PH® Alloy Description 17-4 PH® is a martensitic, chromium-nickel-copper precipitation-hardening stainless steel that provides an outstanding combination of high strength, good corrosion resistance, good mechanical properties at temperatures up to 600ºF (316ºC).

17-4 Stainless Steel 630 Alloy

17-4 Precipitation Hardening also known as Type 630 is a chromium-copper precipitation hardening stainless steel used for applications requiring high strength and a moderate level of corrosion resistance. High strength is maintained to approximately 600 degrees Fahrenheit (316 degrees Celsius). Alloy 17-4 PH is a precipitation hardening martensitic stainless steel with Cu and Nb/Cb additions. 17-4PH Stainless - Delivered Nationwide by West Yorkshire 17-4PH stainless steel stockholders and suppliers, delivering to the whole of the UK. West Yorkshire Steel are suppliers of 17-4PH stainless steel round bar and flat bar. 17-4PH is a corrosion resistant grade which is soft and ductile in the solution annealed condition.

630 (17-4) Precipitation Hardening Stainless Steel Bar

630 is a 17-4 PH martensitic precipitation hardening stainless steel with a unique combination of high strength and good corrosive resistance. Supplied in either the H1075 (H580) aged condition with a tensile strength of 1000 Mpa minimum (HB 311 min.), or the H1150 (H620) double aged condition with a tensile strength of 930 Mpa minimum (HB 277 min.). AMPP Store - Susceptibility of Plasma Nitrided 17-4 PH to It can occur due to the applied stress in the presence of hydrogen sulphide and its associated with the entry of atomic hydrogen into the metal substrate although its mechanisms still unclear.Gap:The martensitic precipitation-hardening stainless steel 17-4 PH (or UNS S17400 - ASTM A564 Type 630 or DIN 14542) at the double-aged condition

ASTM A564 / A564M - 19a Standard Specification for Hot

Type 631 and 632 stainless steels contain a large amount of ferrite in the microstructure and can have low ductility in forgings and large diameter bars. Material of types other than XM-16, XM-25, and Type 630 shall be furnished in the solution-annealed condition, or in ASTM A564 TYPE 630 UNS S17400 17-4PH Round Bar Steel Tubes India continues to expand its product line in ASTM A564 TYPE 630 UNS S17400 17-4PH Round Bar to meet the emerging customer needs, and whereas Steel Tubes India is a A Govt. Of India Recognized Star Export House, ISO 9001, 14001, Ohsas 18001 & PED Certified Company and Awarded by Indian Government for Export Excellence for 6 consecutive Years (2006-2007 & 2007-2008, 2008

Alloy 17-4 PH High Strength Stainless Steel Broder

Alloy 17-4 PH is a high strength stainless steel with good hardness and modest corrosion resistance properties, used widely in marine, food processing and petrochemical industries. We offer 17-4 PH to 1150D; double aged to provide higher tensile strength properties, in sizes 19.05mm dia 171 mm dia ASTM A564 type 630 AMS 5604 Ams 5643 Astm A564 Type 630 Steel Bar Suppliers Mumbai Astm A564 Steel Rod, Astm A564 Type 630 Box Bar, SS Astm A564, Astm A564 Ams 5643 Stockist & Suppliers in India, South Africa, Indonesia, Dubai, Brazil, Sri Lanka, Saudi Arabia and Europe.

Buy Industry Leading All-Purpose a564 type 630 -

About product and suppliers:a564 type 630 are a mixture of iron and chromium which find their application in automotive, textile, defence. shipbuilding, cement, wood, and pulp industry. With such a diverse requirement of a564 type 630, it is very essential that they have a mechanism to prevent themselves from corrosion.This is the reason for missing chromium in the making of a564 type 630. Encore Metals - 17-4PH, T-63017-4PH, T-630. 17-4PH offers a unique combination of properties:high strength, excellent corrosion resistance, good fatigue strength, superior resistance to galling and seizing, easily heat treated by a short, simple low temperature treatment with minimal distortion and no scaling. Parts may be finish-machined before hardening.

MATERIAL DATASHEET 17-4 PH Stainless Steel

ASTM A564 17-4 PH stainless steel heat treated to H900 specification. MIM H900 Heat Treated Typical Mechanical Properties Standard As Sintered H900 H1150 Ultimate Tensile Strength ASTM E8 1050 MPa 1250 MPa 950 MPa 0.2% Yield Strength ASTM E8 800 MPa 1100 MPa 880 MPa SPECIFICATION FOR HOT-ROLLED AND COLD-FINISHED kg] Type 630, Solution,Annealed Cold Finished Ccnterlcss Ground, 1 in. .0 mm] round bar. 10 to 12ft [3.0 to 3.6 m] in length, ASTM A 564 dated . End usc:valve shafts. 4. General Requirements 4.1 In addition to the requirements of this specification, all requirements of the current edition of Specifications A 484/ A 484M shall apply.

SS 17-4 PH UNS S17400 ASTM A564 AMS 5642 MIL-S

  • Low Temperature PropertiesCorrosion ResistanceForgingHeat TreatmentAge HardeningMachiningRemoving Heat TintGrinding and PolishingElevated Temperature UseWeldingRetains relatively good ductility at sub zero temperatures, with impact properties greatly improved at higher ageing temperatures Typical sub zero charpy V-notch impact properties17-4 STAINLESS STEEL AMS 5643 AISI 630 UNS ASTM A564 Type 630 ASME SA564 AMS 5825 Welding Wire AMS 5827 AMS 7474 ASTM A693 ASME SA693 ASTM A705 ASME SA705 17-4 Density:Condition Density Cond A 0.280 #/in3 Cond H900 0.282 #/in3 Cond H1075 0.283 #/in3 Cond H1150 0.283 #/in3 17-4 Stainless Corrosion Resistance: Source High Tensile ASTM A564 Grade 630 Stainless Steel 630, also known as 17-4ph, is famous for it's high tensile strength & high hardness after age hardening treated. We produce strictly as per ASTM A564 standard with different heat treatment conditions, such as condition H900, H1025, H1075, H1100, H1150, H1150M, H1150D etc., mainly used as marine shaft, motor shaft, impreller, offshore industry.

    Stainless Steel 17-4 PH or ASTM A564 (630)

    Browse » Home » ASTM Material » Stainless Steel 17-4 PH or ASTM A564 (630) Stainless Steel 17-4 PH or ASTM A564 (630) 17-4PH / 1.4542 / S17400 air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F Stainless Steel 17-4PH Bar (AMS 5643 / AMS 5622 ASTM A 693 Plate, Sheet and Strip UNS :S17400 17-4 DBLE H1150 ASTM A 564 T 630 Cond H1150D NACE MRO175/ISO 15156-3. 17-4 PH Cond H 1150 ASTM A 564. 17-4 PH Sol AMS 5643 ASTM A 484 AMS 5604 Sheet, Strip Cold Rolled and Plate. AMS 5622 (Vac Melt) Bars (Flat, Hex, Round, Square), Wire, Forgings, Tubing and Rings AMS 5642 Bar

    Stainless Steel 17-4PH:- Harsh Steel

    ASTM A564 Grade 630 ASTM A484 / ASME SA484 ASTM A564 / ASME SA564 ASTM A693 / ASME SA693 Plate, Sheet and Strip Werkstoff 1.4542 X5CrNiCuNb16-4 AFNOR Z6CNU1704 UNS S17400. Harsh Steel export Stainless Steel 17-4 PH to below countries. Steelinox BV 1.4542 630 17-4PH630 (17-4ph) Heat Treatment To ASTM A564/A564M and EN10088-3 After annealing from 1030°C to 1050°C, 1.4542 presents a soft martensitic structure with a hardness of around 35 HRC.

    Chemical Composition ( ASTM A564 Type 630 / 1.4542 /

    type 630 / UNS S17400 / 17-4 PH used for parts requiring corrosion resistance and high strength at room temperature, or at temperatures up to 600°F [315°C]. Boltport uses S17400 round bars to ASTM this specification to manufacturer bolts, screws, studs, rods and custom bolting. Chemical Composition ( ASTM A564 Type 630 / 1.4542 / UNS S17400)